Inconel 600

Time:2019-08-13

Approximate Brand:

GB/T

UNS

Trademark

JIS

W.Nr

NS312

N06600

Inconel600

NCF600

2.4816

 

Chemical constituents of Inconel 600:

alloy

%

Ni

Cr

Fe

C

Mn

Si

Cu

P

S

600

min

72

14

6







max


17

10

0.15

1

0.5

0.5

0.015

0.015


Physical properties of Inconel 600:

density

8.4 g/cm3

Melting point

1370-1425 


Inconel 600 
在常温下合金的机械性能的最小值:

Alloy state

Tensile Strength

Rm  N/mm2

Yield Strength
RP0.2  N/mm2

ElongatSion

A5 %

Brinell hardness

HB

Annealing treatment

550

240

30

≤195

Solution treatment

500

180

35

≤185

 

Inconel 600 alloy has the following characteristics:

1. It has good corrosion resistance to reducing, oxidizing and nitriding media.

2. It has good stress corrosion cracking resistance at room temperature and high temperature.

3. It has good corrosion resistance to dry chlorine and hydrogen chloride gas.

4. Good mechanical properties at sub-zero, room and high temperatures

5. It has good creep fracture strength and is recommended to be used in working environment above 700 C.


Metallographic structure of Inconel  600:

600 is a face-centered cubic lattice structure.

Corrosion resistance of Inconel 600:

600 alloy has corrosion resistance to all kinds of corrosive media. The composition of chromium makes the alloy have better corrosion resistance than nickel 99.2 (alloy 200) and nickel 99.2 (alloy 201, low carbon) under oxidation conditions. At the same time, high nickel content makes the alloy have good corrosion resistance in reduction conditions and alkaline solution, and can effectively prevent stress corrosion cracking of chlorine-iron. 600 alloy has good corrosion resistance in acetic acid, acetic acid, formic acid, stearic acid and other organic acids, and medium corrosion resistance in inorganic acid. It has excellent corrosion resistance in high purity water for primary and secondary recycling in nuclear reactor. In particular, 600 is able to resist the corrosion of dry chlorine and hydrogen chloride, and its application temperature is 650 C. At high temperatures, the annealed and solution-treated alloys have good anti-oxidation and exfoliation properties and high strength in air. The alloy can also resist ammonia, nitriding and carburizing atmosphere, but when the oxidation-reduction conditions change alternately, the alloy will be corroded by some oxidizing medium (such as green death liquid).

Inconel 600 applications include:

1. Thermocouple bushing in corrosive atmosphere

2. Production of vinyl chloride monomers: resistance to chlorine, hydrogen chloride, oxidation and carbonization corrosion

3. Uranium oxidation to hexafluoride: resistance to hydrogen fluoride corrosion

4. Areas of production and use of corrosive alkali metals, especially in environments where sulphides are used

5. Preparation of titanium dioxide by chlorine

6. Production of organic or inorganic chlorides and fluorides: resistance to chlorine and fluorine corrosion

7. Nuclear Reactors

8. Crankneck bottles and components in heat treatment furnaces, especially in carbonization and nitriding atmosphere

9. In the application of catalytic regenerator in petrochemical production, alloy 600 is recommended to obtain longer service life.



Prev :RS-2

Next :Inconel 601

CONTACT US

Address:

No. 17, West Zone, Xiangyun Road, Jixi County, Xuancheng, Anhui, China

Anhui Baitai Steel Industry Co., Ltd. International Sales Department

Contact: MR TOM

CELL: 15868588652

Tel: 0577-86887759

Fax :0577-86887759

Email: tom123631@163.com

SKYPE: tongwenguan813

Contact: Linda Lu

Cell: +86 15167897803

Tel: +86 0577-86699079

Fax:+86 0577-86859555

Email: linda_lfy@163.com

Skype: lfyulrica51

Copyright© Anhui Baitai Steel Industry Co. ,Ltd.